Pressure sensitive adhesives of polymers of cycloaliphatic and phenylalkyl acrylates and vinyl esters

ABSTRACT

Carbocyclic alkyl acrylates and vinyl esters of the general formula: where A is acryloxy (CH2 CHCOO-), methacryloxy (CH2 C(CH3)COO-), or carbovinyloxy (CH2 CHOCO-), R1 is a cycloaliphatic or aromatic group, R2 is a hydrogen atom or lower alkyl, and R3 is an alkylene having at least five carbon atoms, ARE PREPARED, FOR EXAMPLE, BY ALCOHOLYSIS OF LOWER ALKYL ACRYLATES WITH CYCLOALIPHATIC- OR AROMATIC-SUBSTITUTED ALKANOLS OR BY ACYLATION OF SAID ALKANOLS WITH ACRYLOYL OR METHACRYLOYL CHLORIDE, OR BY VINYL ESTER INTERCHANGE OF LOWER VINYL ESTERS WITH CYCLOALIPHATIC- OR AROMATIC-SUBSTITUTED ALKANOIC ACIDS, SAID CARBOCYCLIC ALKYL ACRYLATES AND VINYL ESTERS BEING POLYMERIZABLE MONOMERS USEFUL IN FORMING POLYMERS HAVING UTILITY, FOR EXAMPLE, AS PRESSURE SENSITIVE ADHESIVES.

United States Patent 11 1 Gobran et al.

[ 1 Dec. 2, 1975 [73] Assignee: Minnesota Mining and Manufacturing Company, St. Paul, Minn.

221 Filed: Apr. 19,1973

21 Appl. No.: 352,568

Related US. Application Data [62] Division of Ser. No. 836,946, June 26, 1969, Pat. No.

[52] US. Cl. 428/261; 427/421; 427/428 [51] Int. Cl. C09j 7/02 [58] Field of Search 117/122 P, 122 PF, 122 PA, 117/76 A, 68.5; 260/4109 N OTHER PUBLICATIONS Kulkarni, et al., J. Am. Oil Chemists Soc., 45(6), pp. 465-467, June 21, 1968. Marvel, et al., J. Polymer Science, pt. A, Vol. 2, pp. 2523-2532, (1964).

Marvel, et al., J. Agr. Food. Chem., 13(5), pp. 9-10, 1965.

OConnor, et al., J. Am. Oil Chemists Soc., Vol. 36, pp. 631-635, (1959).

Primary Examiner-Bernard D. Pianalto Attorney, Agent, or Firm-Alexander, Sell, Steldt & DeLaHunt [5 7] ABSTRACT Carbocyclic alkyl acrylates and vinyl esters of the general formula:

where 'A is acryloxy (CH =CHCOO--), methacryloxy (Cl-l =C(Cl-1 )COO), or carbovinyloxy (CH =CHOCO), R is a cycloaliphatic or aromatic group, R is a hydrogen atom or lower alkyl, and R is an alkylene having at least five carbon atoms, are prepared, for example, by alcoholysis of lower alkyl acrylates with cycloaliphaticor aromaticsubstituted alkanols or by acylation of said alkanols with acryloyl or methacryloyl chloride, or by vinyl ester interchange of lower vinyl esters with cycloaliphaticor aromatic-substituted alkanoic acids, said carbocyclic alkyl acrylates and vinyl esters being polymerizable monomers useful in forming polymers having utility, for example, as pressure sensitive adhesives.

7 Claims, No Drawings PRESSURE SENSITIVE ADHESIVES F POLYMERS OF CYCLOALIPI-IATIC AND PI-IENYLALKYL ACRYLATES AND VINYL ESTERS This is a division of application Ser. No. 836,946, filed June 26, 1969, now U.S. Pat. No. 3,751,449.

FIELD OF INVENTION This invention relates acrylates and vinyl esters, and to methods for their preparation. In another aspect, it relates to homopolymers and copolymers of said acrylates and vinyl esters, and to methods for the preparation of said polymers. In another aspect, it relates to copolymers of said acrylates and/or vinyl esters with polymerizable vinyl comonomers, such as conventional lower alkyl acrylates and/or methacrylates, and to methods for the preparation of said copolymers. In a still further aspect, it relates to pressure sensitive adhesives made from homopolymers of said carbocyclic alkyl acrylates and vinyl esters or copolymers of these vinyl compounds with lower alkyl acrylates.

PRIOR ART The relatively long alkylene chain, terminating in a cycloaliphatic or phenyl group, of the acrylates and vinyl esters of this invention, and properties thereof, distinguish them over carbocyclic acrylates and vinyl esters of the prior art. Representative of this prior art are the cyclohexyl acrylates and methacrylates described in J. Org. Chem., Sept., 1950, 4307, in Ind. Eng. Chem. 28 1160 (1936), and in U.S. Pat. No. 2,268,611 and British Patent No. 711,336, the phenyl acrylates described in Ind. Eng. Chem. ibid., the naphthenyl methacrylates in U.S. Pat. No. 2,268,611, the phenemethyl (i.e., benzyl) and phenethyl acrylates described in U.S. Pat. No. 2,219,667, in Ind. Eng. Chem. ibid, in J. Am. Chem., Soc. 72 5199 (1950) and in J. Sci. Ind. Res. (India) 168, 441 (1957), the vinyl 9(10)-phenylstearate described in J. Polymer Sci. A-3 2877 (1965), the acrylates of hydronopoxyalkanols described in J. Polymer Sci. A-l 1543 (1963), and the acrylates of homoterpenylmethyl carbinol and alpha-campholenol described in J. Polymer Sci. A-l 1489 (1967). And though the prior art discloses the use of lower or noncarbocyclic acrylate polymers (e.g., U.S. Pat. No. 3,222,419) and carbocyclic acrylate polymers (e.g., U.S. Pat. No. 3,100,760) in adhesives, such use of the particular carbocyclic acrylate and vinyl ester polymers of this invention are not disclosed or taught.

BRIEF DESCRIPTION OF THE INVENTION Briefly, this invention provides a new class of carbocyclic acrylates and vinyl esters having the general formula:

AR;,CH-R,

where A is acryloxy (CH =CHCOO), methacryloxy l z=C(CH )COO], 0r carbovinyloxy (CH =CHOCO),

R is a cycloaliphatic or aromatic group (e.g.,

phenyl), and

R is a hydrogen atom or lower alkyl (e.g., with l to 6 carbon atoms), and

2 R is an alkylene having at least 4 carbon atoms extending in a straight chain, preferably 5 to 10 such carbon atoms. The cycloaliphatic group preferably will have 5 or 6 ring member atoms, such as cyclopentyl, cyclopentenyl, and cyclohexyl. The aromatic group will be typically phenyl.

The new class of acrylates can be prepared by alcoholysis of lower alkyl acrylates or methacrylates with a cycloaliphaticor aromatic-substituted alkanol, or by the intereaction of acryloyl or methacrylol chloride with said alkanol, or by esterification of acrylic or methacrylic acid with said alkanol. The new class of vinyl esters can be made by vinyl ester interchange of a lower vinyl ester, such as vinyl acetate, with cycloaliphaticor aromatic-substituted alkanoic acids. Said alkanols and alkanoic acids can be represented by the general formula:

where R R and R are as described above for the carbocyclic acrylates, methacrylates, and vinyl esters.

The new classes of acrylates and vinyl esters of this invention have a polymerizable vinyl group and thus can be homopolymerized, or two or more of them can be copolymerized, or one or more of them can be copolymerized with conventional copolymerizable ethylenically unsaturated comonomers, particularly the vinyl compounds capable of vinyl addition reactions, such as the lower alkyl acrylates and methacrylates. Such homopolymers and copolymers are useful, for example, as pressure sensitive adhesives.

DETAILED DESCRIPTION OF THE INVENTION The preferred acrylates, methacrylates, and vinyl esters of this invention can be represented by the formula:

3 where m is an integer of 4 to 12, preferably 5 to 10,

n is an integer from 4 to 9, preferably 6 to 9, and

R is a hydrogen atoms or a lower alkyl of l to 6 carbon atoms.

(The term acrylate as used herein includes acrylate and methacrylate, unless otherwise indicated.)

The acrylates and vinyl esters of formulas II to VII are generally high boiling liquids having freezing points at room temperature or below. They are hydrophobic in nature with their long chain alkylene linkages containing no polar or hydrogen bonding groups and, because of the terminal vinyl group, these acrylates are polymerizable.

The acrylates of this invention can be prepared by various classical procedures such as alcoholysis (ester interchange), acylation, and esterification. Alcoholysis can be carried out by reacting conventional acrylates, particularly the lower alkyl acrylates, with corresponding cyclohexyl-substituted alkanols or phenyl-substituted alkanols in the presence of a strong acid catalyst, such as p-toluenesulfonic acid, concentrated sulfuric acid, concentrated hydrochloric acid, and the like. This reaction is also preferably carried out in the presence of a free radical inhibitor, such as hydroquinone or cuprous chloride, and under a blanket of inert gas such as nitrogen or carbon dioxide to prevent polymerization of the exchanging species. The reaction will generally be run at reflux temperatures of the reaction mixture. The carbocyclic acrylate product can be recovered from the reaction mixture by various conventional procedures, such as fractional distillation under reduced pressure, or solvent extraction.

Where acylation is used to prepare the acrylates, acryloyl or methacryloyl chloride is reacted with, for example, cyclohexylor phenyl-substituted alkanol. where esterification is used, acrylic or methacrylic acid is reacted with the cyclohexylor phenyl-substituted alkanol, or the like.

The vinyl esters of this invention can be prepared by vinyl ester interchange. For example, a lower vinyl ester, such as vinyl acetate, is reacted generally at room temperature with the corresponding cyclohexylor phenyl-substituted alkanoic acid in the presence of a catalyst, such as mercuric acetate, concentrated sulfuric acid, or the like. Recovery of the carbocyclic vinyl ester product can be accomplished by conventional procedures such as fractional distillation and/or extraction, and the like.

The acrylates and vinyl esters of this invention are especially useful as monomers in the preparation of homopolymers, copolymers or two or more of these polymerizable monomers, or copolymers of one or more of these monomers with conventional copolymerizable ethylenically unsaturated compounds such as those containing a vinyl group. The homopolymers and copolymers of one or more of the novel polymerizable monomers are tacky, tough, strong elastomers. As such, they are especially useful in or as pressure sensitive adhesive compositions, having enhanced tack maximum when compared to conventional acrylate adhesive polymers devoid ofa carbocyclic-terminated, longchain alkylene group. They adhere well to Kraft paper, and other adherends, under load despite the fact that they are essentially hydrophobic in nature and contain no polar or hydrogen bonding side chains, in addition to those associated with ester groups, which are generally considered essential to provide the prerequisite 4 balance of cohesive strength and compliance necessary for high values in a typical packaging application.

The homopolymcrization of the novel polymerizable monomers of this invention, or the copolymerization of one or more of such monomers, is preferably carried out in organic solvent solution, or the polymerization can be carried out in suspension or in emulsion, in the presence of a free radical or redox initiator. Preferably, polymerization is carries out in emulsion in the presence of an oxidation-reduction initiator system, such as potassium persulfate and sodium bisulfite.

As mentioned above, the acrylates and vinyl esters of this invention can be copolymerized with other polymerizable ethylenically unsaturated monomers, particularly vinyl compounds. A preferred class of such comonomers are the acrylic and methacrylic acids and their esters of the general formula CH =C(R)COOR, where R is a hydrogen atom or methyl, and R is a hydrogen atom or an n-alkyl or a secondary or branched alkyl, such alkyl groups having from 1 to 18 carbon atoms. These acrylic ester comonomers representatively include methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, pentyl, hexyl, Z-ethylhexyl, heptyl, octyl, isooctyl, nonyl, decyl, dodecyl, acrylates or methacrylates and the like. copolymerization of the acrylates and vinyl esters of this invention with two or more of these conventional acrylates and methacrylates can be similarly carried out by the free radical initiated solution or emulsion polymerization. The resultant copolymers can be recovered again by precipitation if solution polymerization is used or by coagulation if emulsion polymerization is used. Such copolymers, like the above described homopolymers and copolymers of two or more of the novel methacrylate, acrylates, and vinyl esters of this invention, are generally solid, tough, high molecular polymeric materials with relatively high degree of tackiness, making them also suitable in pressure sensitive adhesives.

Other conventional polymerizable monomers which can be copolymerized with one or more of the novel polymerizable monomers of this invention include styrene, alkyl and alkoxy styrenes, such as alpha-methyl styrene and methoxy-styrene, chlorostyrenes, cyanoand carboxy-styrenes, vinyl pyridines, vinyl quinolines, acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, vinyl acetate, higher vinyl esters such as vinyl laurate, and vinyl benzoate, vinyl chloride, vinylidine chloride, olefines such as ethylene and propylene, and conjugated dienes such as. 1,3-butadiene, isoprene, chloroprene, 2,3-dimethyl-1,3-butadiene, and the like.

The manipulative polymerization procedures to be used in preparing the polymers of this invention are old in the art and reference is made to Preparative Methods of Polymer Chemistry, by W. R. Sorenson and T. W. Campbell, published 1961 by lnterscience Publishers, lnc., N. Y., (especially Chapter 4), and Vinyl and Related Polymers, by C. E. Schildknecht, published 1952 by John Wiley & Sons, lnc., N. Y.

As mentioned above, we are particularly interested in using the novel acrylates and vinyl esters of this invention to make polymers having a high degree of inherent tackiness and useful in pressure sensitive adhesives. Such pressure sensitive adhesive compositions are generally prepared by dissolving or dispersing said polymers in an organic liquid solvent such as ethyl acetate, benzene, toluene, chlorobenzene, methylene chloride, tetrahydrofuran, and the like, including mixtures thereof, the total resin solids content in resultant solution or dispersion varying, for example, from to 30 percent by weight. The original polymerization latex itself can be used, and, if desired, such solvents added thereto to obtain the desired solids content.

The resultant polymers are sufficiently tacky and there is no need to mix them with tackifiers, which would usually result in loss of strength.

The adhesive solution or dispersion can be applied to virtually an unlimited variety of substrates, such as paper, cloth, metal sheets and foils, cellophane, wood, and plastic films and sheets, such as those derived from polyethylene terephthalate, polystyrene, rubber hydrochloride, polyethylene, polypropylene, polyvinyl chloride, and polyvinylidene chloride and the like. Any coating technique can be used to apply the adhesive to such substrates. For example, they can be sprayed onto a substrate or applied by the use of any mechanical coating process, such as air knife, trailing blade, reverse roll, or graveure coating technique. The adhesive will usually be applied at coating weight which will give a dry film thickness of about 1 to 5 mils. The coating weights at which the adhesives are applied will, of course, vary according to specific end use application.

It is also within the scope of this invention to apply the adhesive to flexible backing sheets, such as metal, textile, paper, natural or synthetic sheet and tape materials, such as cloth, cellulose and cellulose derivative sheets, and tapes.

EXAMPLES The objects and advantages of this invention are further illustrated by the following examples, but it should be understood that the particular materials used in these examples, and the amounts thereof, and other conditions and details recited in these examples, should not be construed to unduly limit this invention.

EXAMPLE 1 In a 500 ml round-bottom flask equipped with a nitrogen inlet, a 24-inch insulated Vigreaux column, and a total reflux head, were placed 113.2 g. (0.445 mole) 10 cyclohexylundecyl alcohol, 200 ml. (187.5 g., 1.88 mole) methyl methacrylate, 5.0 g. cuprous chloride, and 2 ml. conc. sulfuric acid. Heat was applied and the methyl methacrylate-methanol azeotrope (85% methanol) boiling at 6465C. was removed continuously until the temperature at the still head rose to 98100C. The reaction mixture was then cooled, 6.0 g. of potassium carbonate added to neutralize the acid, and the excess methyl methacrylate removed in vacuo. The residue was filtered and distilled under nitrogen in the presence of cuprous chloride to give 72.0 g. of 10- cyclohexylundecyl methacrylate, b.p. 146-160C. at 0.060 mm.

EXAMPLE 2 The general procedure for Example 1 was employed using IO-phenylundecanol as the alcohol and a 4-molar excess of methyl acrylate to provide IO-phenylundecyl acrylate, b.p. 136C. at 0.05 mm.

EXAMPLE 3 To a mixture of 58 g. (0.30 mole) 7-phenylheptanol, 43.2 ml. triethylamine, and 200 ml. dry benzene, cooled to 10C. with an ice bath, 31.6 g. (0.30 mole) of methacryloyl chloride was added dropwise with stirring while maintaining the temperature of the mixture at 1015C. After the addition was complete, the reaction mixture was allowed to stir at ambient temperature overnight. The resulting slurry was then washed thoroughly with water, the benzene layer dried over anhydrous magnesium sulfate and concentrated in vacuo. The residue was distilled in the presence of cuprous chloride to give 7-phenylheptyl methacrylate, b.p. 112113C. at 0.5 mm.

EXAMPLE 4 To a solution of 130 g. of IO-phenylundecanoic acid in 258 g. of vinyl acetate, were added, in order, 2.6 g.

of mercuric acetate, and 0.65 g. of cone. sulfuric acid.

The dark solution was stirred at room temperature for five days, at which time 5 g. of sodium acetate were added. The remaining vinyl acetate was removed in vacuo and the residue distilled to give 87 g. (60%) of vinyl 10-phenylundecanoate, b.p. 105l25C. at 0.15

EXAMPLES 5-8 The following monomers were prepared in a manner 25 similar to that described in the above examples.

Monomer b.p., C.

lo-phenylundecyl methacrylate l39144 at 0.025 mm lo-cyclohexylundecyl acrylate 148 at 0.10 mm.

l48-l 50 at 0.30 mm 109-1 13 at 0.10 mm vinyl-10-cyclohexylundecanoate 5-phenylpentyl methacrylate EXAMPLE 9 A reaction vessel was charged with 23.5 g. of the 10- cyclohexylundecyl methacrylate, ml. of deoxygenated water and 2.0 g. of an alkylaryl polyoxyethylene wetting agent (Sandozin N1). After purging with nitrogen, there was added 0.100 g. of potassium persulfate and 0.050 g. of sodium bisulfite, and the polymerization mixture was stirred under a blanket of nitrogen for 16 hours at room temperature. The emulsion was coagulated by pouring it into 400 m1. of methanol, the resulting solid polymer was washed with methanol and purified by two precipitations from tetrahydrofuran' with methanol. The solid poly(10-cyclohexylundecyl methacrylate) polymer was tough, tacky elastomer exhibiting a glass transition, Tg, at 47C. and the intrinsic viscosity of 2.80 dl/g in tetrahydrofuran.

EXAMPLE 10 EXAMPLE 1 1 A reaction vessel was charged with 21.6 g. (0.075 mole) of the vinyl IO-phenylundecanoate prepared in Example 7, ml. of deoxygenated water, and 4 g. of sodium polyethyleneglycol aryl sulfonate wetting agent (Triton X-200). After purging with nitrogen, 0.100 g.

7 of potassium persulfate was added, the emulsion heated to 6570C. and 14.8 g. (0.075 mole) Z-ethylhexyl acrylate was added dropwise with stirring over a period of two hours. When the addition was complete, stirring 8 Solutions of approximately 10 percent by weight of each of the polymers in tetrahydrofuran were prepared and knife coated into polyethylene terephthalate (Mylar) or cellophane film at a coating thickness of from 10 was continued at 6570C. for 22 hrs. The emulsion to 15 mils and coating weights of 2.5 to 3.75 grains/sq. was coagulated by pouring into excess methanol and in. Adhesive properties were evaluated as follows: tack the solid copolymer, poly(vinyl IO-phenylundecanomaxima were determined as a function of temperature ate-co-2-ethylhexyl acrylate), was separated by centrifin a modified Kendall tack tester utilizing a l/l6 inch ugation. Purification by two precipitations from methadiameter stainless steel probe at a pressure of 100 nol gave 14.0 g of tough, tacky elastomer having an ing./cm and a dwell time of one second. trinsic viscosity of 1.44 dl/g. in tetrahydrofuran. Nuclear magnetic resonance spectroscopy indicated a molar ratio of 3:7 for vinyl lO-phenylundecanoate: 2- P01 mar 1 if? ethylhexyl acrylate in the copolymer. y n

Poly( 1 O-phenylundecyl 2.10 170 EXAMPLES 12-17 acrylate) Poly( lO-cyclohexylundecyl 3.10 220 The following illustrates the properties of homopolyy d I 2 63 180 mers prepared by procedures described above. z gggig l Bey Intrinsic Glass viscosity transition Polymer 1], /g TE C- 12 Poly( l0-phenylundecyl acrylate) 2.80 43 13 poly( lO-cyclohexylundecyl acrylate) 3.00 -55 14 poly(vinyl lO-cyclohexylundecanoate) oil 15 poly(S-phenylpentyl methacrylate) crosslinked 7 16 poly(7-phenylheptyl methacrylate) 1.70 17 poly(vinyl IO-phenylundecanoate) 0.45

All of these polymers were compliant, amorphous elastomers of high molecular weight, though the molecular msgg fizgi weight of Exs. 14 and 17 were relatively lower. Poly(vinyl IO-phenyl- 0.8 145 undecanoate-co-ethyl EXAMPLE l8 acrylate) Poly(vinyl lO-phenyl- 2.30 I75 A copolymer of vinyl IO-phenylundecanoate and nf y y z butylacrylate was prepared essent ally by the procefiz z i lo phenyl 226 120 dure outlined in Example 11 utilizing 14.4 g. (0.05 undecanoate-co-n-butyl acrylate) mole) of vinyl 10 phenylundecanoate, 6.6 g. (0.05 Poly(lo cyclohexylundecyl 3.50 280 mole) of n-butyl acrylate, 60 ml. of deoxygenated waac,y1me co.n bmyl ter, 3 g. of Triton X-200 wetting agent, and a redox cat- 40 P 1 3 6 I h l d I 4 5 8o alyst of 0.100 g. of potassium persulfate and 0.060 g. of g ggg g igg sodium bisultite at room temperature. Recovery of the methacrylate) copolymer with tetrahydrofuran and purification of two precipitations from methanol resulted in 15 g. of copolymer having an intrinsic viscosity of 2.26 dl/g. in

. EXAMPLE 23 tetrahydrofuran. Nuclear magnetic resonance spectros- I copy indicated a molar ratio of 15:84 for n-butylacry- This example illustrates the evaluation of two of the late: vinyl IO-phenylundecanoate in the copolymer. above prepared polymers in a packaging application. Sample tapes for evaluation were prepared as de- EXAMPLES l9'2l scribed in Example 22 and used to determine their The table below illustrates copolymers that have package sealing ability. Kraft paper bags filled with 2- been prepared from the above described monomers pound quantities of beans were closed with four folds using the polymerization technique of Example 18. and sealed with a two-inch long strip of half-mch tape applied across the fold. The tape was applied with a light stroking motion of the fingertips. Tape samples of P-* poly( 10-cyclohexylundecylmethacrylate) (Example 9) Momma Comonome' (molar) and poly( l0-phenylundecyl methacrylate (Example 19 vinyl y y ethyl acrylate 112 10) when utilized in this test adhered firmly and comundecanoate 20 lO-cyclohexylundecyl iso-octyl meth- 4.15 1:1 pletely h first and the bfigs F acrylate acrylate sealed. Various modifications and alterations of this inlo'clyiwhexylundecyl acrylate vention will become apparent to those skilled in the art acry a 6 without departing from the scope and spirit of this in vention, and it should be understood that this invention is not to be unduly limited to the illustrative embodimerit set forth herein.

EXAMPLE 22 This Example illustrates the preparation and evaluation of the above-prepared polymers as adhesives.

What is claimed is: l. A pressure sensitive adhesive sheet material comprising a flexible backing sheet having applied thereto a 9 pressure sensitive layer of a polymer of a compound of the formula where A is acryloxy or methacryloxy, R is cyclohexyl, cyclopentyl, or cyclopentenyl, R is a hydrogen atom or lower alkyl, and R is an alkylene having at least 4 carbon atoms extending in a chain.

2. The sheet material of claim 1, wherein R is cyclohexyl, R is a hydrogen atom, and R is an alkylene with 5 to carbon atoms extending in a chain.

10 3. The sheet material of claim 1, wherein A is acryloxy.

4. The sheet material of claim 1, wherein A is methacryloxy.

and n-butyl acrylate.

UNITED STATES PATENT AND TRADEMARK OFFICE CETIFTQATE F CGRRECTION PATENT NO. 3,92 T,O T3

DATED December 2, 1975 INVENTOR S Ramsis Gobran, Hanspeter Knoepfel, and

r S ncer F. .S' lver r e n It rs cerrrfred tEaTerror appears 111%h8 above-rrien'irfled patent and that sard Le rers Paien are hereby corrected as shown below:

Column 3, line 37, "Where" should read Where Column 6, line 22, "25" before "similar" should be omitted;

Column 8, line 57, "methacrylate" should read methacrylate) Signed and Sealed this eleventh D a'y Of May 1 976 [SEAL] A tresr:

RUTH C. MASON C. MARSHALL DANN K ff fl ('ununissimu'r uflan'ms umi Trademarks 

1. A PRESSURE SENSITIVE ADHESIVE SHEET MATERIAL COMPRISING A FLEXIBLE BACKING SHEET HAVING APPLIED THERETO A PRESSURE SENSITIVE LAYER OF A POLYMER OF A COMPOUND OF THE FORMULA
 2. The sheet material of claim 1, wherein R1 is cyclohexyl, R2 is a hydrogen atom, and R3 is an alkylene with 5 to 10 carbon atoms extending in a chain.
 3. The sheet material of claim 1, wherein A is acryloxy.
 4. The sheet material of claim 1, wherein A is methacryloxy.
 5. The sheet material of claim 1, wherein said polymer is poly(10-cyclohexylundecyl acrylate) or poly(10-cyclohexylundecyl methacrylate).
 6. The sheet material of claim 1, wherein said polymer is a copolymer of 10-cyclohexylundecyl acrylate and iso-octylmethacylate.
 7. The sheet material of claim 1, wherein said polymer is a copolymer of 10-cyclohexylundecyl acrylate and n-butyl acrylate. 